FOTECH

Copolymer PVDF FL-2606

Group PVDF
Min. Order 100 kilogram
Terms of Payment L/C, D/A, D/P, T/T
Update Time 2016-07-01
Item specifics
CAS No.24937-79-9
TypeSynthetic Resin and Plastics
Purity99%

                                      Copolymer PVDF FL-2606


Characteristic

General

Features

Copolymer, Medium and low viscosity

Uses

Extruded pipe, Bar, Plate

Forms

Translucent white particles

Physical Properties

Melt Flow Rate(g/10min)

4 ~ 8

Load 5kg, 230℃, ASTM D1238

Density(g/cc)

1.77~1.80

ASTM D792

Water Absorption(%)(Time 24 hr)

≤0.040

ISO 62

Mechanical Properties

Yield Strength(MPa)

30~40

50mm/min,ASTM D638

Break Strength(MPa)

20~35

50mm/min,ASTM D638

Elongation at Yield(%))

10~15

50mm/min,ASTM D638

Elongation at Break(%)

200~600

50mm/min,ASTM D638

Hardness, Shore D

70~75

ASTM D2240

Thermal Properties

Melting Point(℃)

158~166

ASTM D3418

Crystallization Temperature(DSC peak)(℃)

115~130

ASTM D3418

Glass Transition Temperature, Tg(℃)

-32

ASTM E1356

Vicat Softening Point(℃)

90~105

ASTM D1525


Process safety instructions

(1). This product should be processed under 260℃, to avoid producing toxic gases;

(2). PVDF has good fire resistance and smoke inhibition property, however, when meets with fire, it will release toxic hydrogen fluoride gas and fluorocarbon compounds;

(3). Operators should take good care of personal protection during the use procedure and processing.


Packaging and storage

(1). PVDF is sealed in plastic bag with 25kg net weight per bag and then put into drum or cardboard.

(2). It must be stored in clean, cool, dry place.